high wear resistant Bimetal Cladding Pipe and bend

Bimetal Clad Pipe good mechanical impact convenient in connection with standing high pressure good resistance

 

1. Manufacturing Process of Bimetal Cladding Steel Pipe and Bend:     

Bimetal Cladding Steel Pipe and Bend are cast with mold vanishing vacuum suction casting cladding process. 

Outer of straight pipe is common steel pipe, cladding realized by forming high chromium lining via 

centrifugal forming technique. 

Outer of bend uses hot-bending bend and lining is cast with high chromium cast iron.

 Bends and other profile sections can be cladded in whole and this process has changed the traditional practice 

to fabricate bend and other profile sections by drawing polyline without changing flow pattern of material inside piping,

greatly reducing conveyance resistance of material.

2. Advantages 

Compared with Wear Resistant Alloy Cast Iron, Alloy Cast Steel, General Clad Steel Pipe and Cast Stone Pipe:

1. Good wear-resistance, giving full play to wear-resistance of high chromium cast iron.

2. Withstanding high pressure: 

Bimetal Cladding Pipe and bend can be used for any pressure rating.

 Close bonding of outer and lining by adopting special process make cladding interlayer molten-joint to ensure reliable operation. 

3. Good mechanical impact and thermal impact resistance property.

4. Convenient in connection for installation:

Bimetallic cladding pipe and bend can be cut and welded as you like.

3. Physical Properties of Bimetal Cladding Steel Pipe and Bend: 

Flexure  Strength	Tensile  Strength	Elongation	Cross Section  Stretch Ratio	Impact Toughness	Hardness  of Wearable Layer	Hydrostatic  Testing Pressure
MN/square m	MN/square m	%	%	J/square cm	HRC	Mpa
>610	>700	5	5.1	>15	>38	5.6-12.9

high wear resistant Bimetal Cladding Pipe and bend